Sifat Kayu Lapis yang Dibuat dari Lima Jenis Kayu Asal Riau

  • Achmad Supriadi Pusat Penelitian dan Pengembangan Hasil Hutan, Jl. Gunung Batu No. 5, Bogor 16118
  • Deazy Rachmi Trisatya Pusat Penelitian dan Pengembangan Hasil Hutan, Jl. Gunung Batu No. 5, Bogor 16118
  • Ignasia Maria Sulastiningsih Pusat Penelitian dan Pengembangan Hasil Hutan, Jl. Gunung Batu No. 5, Bogor 16118
DOI: https://doi.org/10.18343/jipi.25.4.657

Abstract

The objective of this study was to determine the physical and mechanical properties of plywood made of punak (Tetramerista glabra Miq.), meranti bunga (Shorea teysmanniana Dyer ex Brandis), mempisang (Alphonsea spp.), suntai (Palaqium burckii H.J.L.), and pasak linggo (Aglaia argentea Blume). Liquid urea formaldehyde (UF) was used as an adhesive. Data analysis was carried out using a completely randomized design. Results showed that the moisture content and density of plywood produced in this study were around 10.4-10.95% and 0.65 to 0.93 g/cm3, respectively. The modulus of elasticity (MOE) and modulus of rupture (MOR) of plywood produced were between 63.371-123.548 kg/cm2 and 517-1.052 kg/cm2, respectively. It was also found that the tensile strength and bonding strength of the plywood produced were 461.6-1.095 kg/cm2 and 18.97-31.79 kg/cm2, respectively. It was recorded that moisture content and the bonding strength of the plywood produced met the Indonesian National Standard of Plywood. Among others, plywood produced from pasak linggo showed a superior quality. Referring to statistical analysis, it was confirmed that physical and mechanical properties of plywood were significantly affected by wood species, except moisture content.

Keywords: mechanical properties, physical properties, plywood, Riau wood species

Downloads

Download data is not yet available.

References

[ASTM] American Society for Testing and Materials. 1995. Standard Test Methods for Structural Panels in Tension. Annual Book of ASTM Standard. ASTM D 3500-90. Philadelphia.

Arsad E. 2011. Sifat fisik kayu lapis berbahan baku kayu akasia (Acacia mangium Willd.) dan kelampayan (Anthocephalus spp.). Jurnal Riset Industri Hasil Hutan. (3)2: 16. https:// doi.org/10.24111/jrihh.v3i2.1188

Bal BC, Bektay I. 2014. Some Mechanical Properties of Plywood Produced from Eucalyptus, Beech, and Poplar Veneer. Maderas. Ciencia y tecnologia 16(1): 99108. https://doi.org/10.4067/S0718-221 X2014005000009

Direktorat Jenderal Pengelolaan Hutan Produksi Lestari (PHPL). 2019. Jumlah dan kapasitas ijin produksi industri primer hasil hutan kayu (IPHHK) di atas 6.000 m3/tahun per Provinsi sampai dengan Mei 2019. Ditjen PHPL Kementerian Lingkungan Hidup dan Kehutanan Jakarta.

Hadi F. 1996. Pengaruh kadar ekstender dan variasi waktu tekan terhadap keteguhan dan daya tahan rekat kayu lapis jenis meranti merah (Shorea spp.) dan kapur (Dryobalanops sp.). [Skripsi]. Samarinda (ID): Universitas Mulawarman.

Haygreen JG, Bowyer JL. 1993. Forest Product and Wood Science, an Introduction. Iowa (US): Iowa State University Press.

Iskandar MI, Kliwon S, Sutigno P. 1990. Sifat Venir dan Kayu Lapis 8 Jenis Kayu dari Sulawesi Tengah. Jurnal Penelitian Hasil Hutan 8(4): 150156.

Iskandar. 1990. Keteguhan rekat kayu meranti merah (Shorea spp.) dengan menggunakan perekat styrofoam. [Skripsi]. Bogor (ID): Institut Pertanian Bogor.

Iskandar MI, Supriadi A. 2017. Pengaruh jenis kayu dan jumlah lapisan terhadap sifat venir lamina. Jurnal Ilmu Pertanian Indonesia. 22(1): 3440. https://doi.org/10.18343/jipi.22.1.34

[JAS] Japanese Agricultural Standard. 2008. Japanese Agricultural Standard for Plywood. Ministry of Agriculture, Forestry and Fisheries.

Kelly MW. 1977. Critical literature review of relationship between processing parameters and physical properties of particleboards. General Technical Report FLL-10.

[KLHK] Kementerian Lingkungan Hidup dan Kehutanan. 2018. Statistik Kementerian Lingkungan Hidup dan Kehutanan 2017. Jakarta (ID).

Kliwon S, Iskandar MI. 2008. Teknologi Kayu Lapis dan Produk Sekundernya. Pusat Penelitian dan Pengembangan Hasil Hutan. Bogor (ID): Badan Penelitian dan Pengembangan Kehutanan.

Mardikanto T.R., Karlinasari L & Bahtiar ET. 2009. Sifat Mekanis Kayu. Fakultas Kehutanan IPB, Bogor.

Muhammad-Fitri S, Suffian M, Wan-Mohd-Nazri WAR & Nor-Yuziah Y. 2018. Mechanical Properties of Plywood from Batai (Paraserianthes falcataria), Eucalyptus (Eucalyptus pellita) and Kelempayan (Neolamarckia cadamba) with Different Layer and Species Arrangement. Journal of Tropical Forest Science 30(1): 5866. https://doi.org/ 10.26525/jtfs2018.30.1.5866

Alam DMN, Islam MN, Rahman KS & Alam MR. 2012. Comparative Study on Physical and Mechanical Properties of Plywood Produced from Eucalyptus (Eucalyptus camaldulensis Dehn.) and Simul (Bombax ceiba L.) Veneers. Research Journal of Recent Sciences 1(9): 5458.

Perry TD. 1994. Modern Wood Adhesives. London (EN): Pitman and Sons.

Praptoyo H. 2010. Sifat anatomi dan sifat fisika kayu mindi (Melia azedarach Linn) dari hutan rakyat di Yogyakarta. Jurnal Ilmu Kehutanan. (4)1: 2127.

Rachman O, Hardjo, S, Suwirman, M. 1997. Perbaikan Teknik pelengkungan rotan melalui perendaman dengan larutan dimetil sulfoksida. Buletin Penelitian Hasil Hutan. 15(4): 299311.

Ruhendi S, Koroh DN, Syamani FA, Yanti H, Nurhaida, Saad, S, Sucipto T. 2007. Analisis Perekatan Kayu. Bogor ID): Institut Pertanian Bogor.

Santoso A, Firmanti A, Karno RA. 1998. Pengaruh penambahan ekstender dalam perekat fenol formaldehida terhadap keteguhan rekat kayu lapis tusam. Buletin Penelitian Hasil Hutan. 15(5): 337347.

Santoso A, Sulastiningsih IM, Pari G, Jasni. 2016. Pemanfaatan ekstrak kayu merbau untuk perekat produk laminasi bambu. Jurnal Penelitian Hasil Hutan. 34(2): 89100. https://doi.org/10.20 886/jphh.2016.34.2.89-100

Santoso S. 2018. SPPS Versi 25. Jakarta (ID): PT. Elex Media Komputindo.

[SNI] Standar Nasional Indonesia. 2000. Kayu lapis penggunaan umum (SNI 01-5008.2-2000). Jakarta.(ID): Badan Standarisasi Nasional.

Sulastiningsi IM, Sutigno P. 1992. Pengaruh Campuran Jenis Kayu terhadap Beberapa Sifat Kayu Lapis. Jurnal Penelitian Hasil Hutan 10(3): 9096. https://doi.org/10.20886/jphh.2005.23. 1.15-22

Sulastiningsih IM, Hadjib N, Santoso A. 2005. Pengaruh lapisan kayu terhadap sifat bambu lamina. Jurnal Penelitian Hasil Hutan. 23(1): 1522.

Sulastiningsih IM, Krisdianto. 2012. Physical and mechanical properties of combination plywood sengon and bamboo. Proceedings of International Seminar Strategies and Challenges on Bamboo and Potential Non Timber Forest Products (NTFPs) Management and Utilization. Center for Forest Productivity Improvement Research and Development. Bogor (ID): 131135.

Published
2020-10-27
How to Cite
SupriadiA., TrisatyaD. R., & SulastiningsihI. M. (2020). Sifat Kayu Lapis yang Dibuat dari Lima Jenis Kayu Asal Riau. Jurnal Ilmu Pertanian Indonesia, 25(4), 657-663. https://doi.org/10.18343/jipi.25.4.657
Issue
Vol. 25 No. 4 (2020): Jurnal Ilmu Pertanian Indonesia
Section
Articles

This journal is published under the terms of the Creative Commons Attribution-NonCommercial 4.0 International License. Authors who publish with this journal agree to the following terms: Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution-NonCommercial 4.0 International License. Attribution — You must give appropriate credit, provide a link to the license, and indicate if changes were made. You may do so in any reasonable manner, but not in any way that suggests the licensor endorses you or your use. NonCommercial — You may not use the material for commercial purposes.

Crossref
Scopus
Google Scholar
Europe PMC