Candlenut shell as a lignocelullose raw material is a potential by-product for produce activated charcoal. It’s quality are affected by raw material and activated process i.e. temperature, activation time and activating agent.  This paper intends to study the properties of activated charcoal made from candlenut shell. Candlenut shell was carbonization at 500 °Cfor 5 hour. Then activated using phosphoric acid in three different temperatures: 600 °C, 700 °C and 800 °C, in the duration time of 90, 120 and 150 minutes.  The result shows that candlenut shell activated charcoal more influence of temperature than activation time. Overall, the activated charcoal met the Indonesian Standard requirement for commercialised activated charcoal with optimation activation at 800 °C  for 120 minute.   Keywords :    Candlenut shell, activated charcoal, optimation, activation, phosphoric acid

Saptadi DARMAWAN; Gustan PARI; Kurnia SOFYAN

Candlenut shell as a lignocelullose raw material is a potential by-product for produce activated charcoal. It’s quality are affected by raw material and activated process i.e. temperature, activation time and activating agent. This paper intends to study the properties of activated charcoal made from candlenut shell. Candlenut shell was carbonization at 500 °Cfor 5 hour. Then activated using phosphoric acid in three different temperatures: 600 °C, 700 °C and 800 °C, in the duration time of 90, 120 and 150 minutes. The result shows that candlenut shell activated charcoal more influence of temperature than activation time. Overall, the activated charcoal met the Indonesian Standard requirement for commercialised activated charcoal with optimation activation at 800 °C for 120 minute. Keywords : Candlenut shell, activated charcoal, optimation, activation, phosphoric acid

Saptadi DARMAWAN
Gustan PARI
Kurnia SOFYAN

Abstract

Candlenut shell as a lignocelullose raw material is a potential by-product for produce activated charcoal. It’s quality are affected by raw material and activated process i.e. temperature, activation time and activating agent. This paper intends to study the properties of activated charcoal made from candlenut shell. Candlenut shell was carbonization at 500 °Cfor 5 hour. Then activated using phosphoric acid in three different temperatures: 600 °C, 700 °C and 800 °C, in the duration time of 90, 120 and 150 minutes. The result shows that candlenut shell activated charcoal more influence of temperature than activation time. Overall, the activated charcoal met the Indonesian Standard requirement for commercialised activated charcoal with optimation activation at 800 °Cfor 120 minute.

Keywords : Candlenut shell, activated charcoal, optimation, activation, phosphoric acid

Issue

Vol. 2 No. 2 (2009): Jurnal Ilmu Teknologi Hasil Hutan

Section

Articles